Applications in the drinking water sector; hose applications

Processing Method:
Injection Molding, Extrusion
Color / RAL DESIGN:
translucent
 
 
Availability:
Globally
Manufacturing Site:
Germany

Typical applications

  • Shower hoses
  • Hoses for household appliances
  • Jet former
  • Grip applications
  • Soft touch
  • Seals, functional and design elements in sanitary sector

 

Material features

  • Low kinking tendency
  • Optimized mechanical properties
  • Adhesion to PP
  • Alternative material to PVC-P
  • Surface with low sensitivity to dirt
  • Plasticizer free
  • Resistance to microbes
  • Precoloration in all colors

 

Regulations / Approvals

  • Regulation (EU) No 10/2011
  • DVGW Arbeitsblatt W270
  • KTW
  • ACS (DGS/VS4 n° 200/232)
  • WRAS: BS6920-1:2000 and/or 2014 cold water (23 °C)
  • WRAS: BS6920-1:2000 and/or 2014 warm water (60 °C)

 

X

SHARE FILE

Send
Please choose language of datasheet
PDF file - 1MBEnglish
PDF file - 1MBDeutsch
PDF file - 1MB中文
PDF file - 1MBEspañol
PDF file - 1MBFrançais
PDF file - 1MB日本語
PDF file - 1MB한국어
PDF file - 1MBPolski
PDF file - 1MBItaliano
Please choose language of datasheet
PDF file - 1MBEnglish
PDF file - 1MBDeutsch
PDF file - 1MB中文
PDF file - 1MBEspañol
PDF file - 1MBFrançais
PDF file - 1MB日本語
PDF file - 1MB한국어
PDF file - 1MBPolski
PDF file - 1MBItaliano
Americas (English) PDF fileSafety Data Sheet
Asia (English) PDF fileSafety Data Sheet
Asia (中文) PDF fileSafety Data Sheet
Asia (한국어) PDF fileSafety Data Sheet
Asia (日本語) PDF fileSafety Data Sheet
PDF file W270-TF5WHA-TF8WHA-2020-2025-en-
PDF file KTW-TF5WHA-TF8WHA-2020-2025-en-
PDF file WRAS-TF5WHA-TF8WHA-
PDF file ACS-TF5WHA-TF8WHA
PDF file KTW-TF5WHA-TF8WHA
Value Unit Standard
Hardness 60 Shore A DIN ISO 48-4
Density 0.900 g/cm3 DIN EN ISO 1183-1
Tensile Strength1 16.0 MPa DIN 53504/ISO 37
Elongation at Break1 750 % DIN 53504/ISO 37
1Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min.
All values published in this data sheet are rounded average values.
The expected shelf life of the TPE granules is a minimum of 24 months from the date of delivery, provided that the storage instructions are followed and the product is kept in the unopened original KRAIBURG TPE packaging.
Dry conditions at room temperature (below 40 °C/ 104 °F), away from heat sources and direct sunlight, must be maintained for proper storage. Contact with nitrogen oxides during storage should be avoided.
For further information and individual custom solutions please contact our customer service.

Processing Guideline Injection Molding
Cylinder Temperature 180 - 190 - 200 °C, max. 235 °C (360 - 370 - 390 °F, max. 445 °F)
Hotrunner Hot runner temperatures: 200 - 235 °C (390 - 455 °F). The runner should be empty after a maximum of 2 - 3 shots.
Injection Pressure 200 - 1000 bar (2900 - 14504 psi) (depending on the size and weight of the part).
Injection Rate In general, the fill time should not be more than 1–2 seconds.
Hold Pressure We recommend to derive the optimum hold pressure from determining the solidification point, starting with 40 % - 60 % of the required injection pressure.
Back Pressure 20 - 100 bar; if color batches are used, higher back pressure is necessary.
Screw Retraction If an open nozzle is used processing with screw retraction is advisable.
Mold Temperature 25 - 40 °C (77 - 104 °F) The use of mold release agents can have an influence on the microbiological resistance.
Predrying Due to better processing behavior pre-drying is recommended. Drying conditions: 60°C-80°C for 2-4 hrs.
Needle Valve With materials < 50 Shore A the use of a needle valve is advisable.
Screw Geometry Standard 3-zone polyolefine screw.
Residence Time The residence time is to be set as short as possible with a maximum of 10 minutes.
Cleaning Recommendation For cleaning and purging of the machine it is appropriate to use polypropylene or polyethylene. Machine must be PVC-free.
Processing Guideline Extrusion
Cylinder Temperature 160 - 180 - 200 °C; max. 235 °C (320 - 360 - 390 °F; max. 455 °F).
Screw Geometry Standard three-zone screw (e.g. polyolefin screw). The screw must be able to provide sufficient shearing.
L/D Ratio At least 25
Compression Ratio At least 3.5 : 1
Screens / Breaker Plate A breaker plate and a screen pack are generally recommended in the extruder configuration in order to increase pressure.
Die Land <= 3 mm ( <= 0,12 in.)
Extruder Head Ca. 200 °C (390 °F)
Die Temperature Ca. 200 - 230 °C (390 - 450 °F)
Predrying Pre drying of the material is not necessary; if surface moisture forms as a result of changes in temperature, the material should be dried for 2 - 4 hours at 60 - 80 °C (140 - 175 °F).
Calibration Generally not necessary; support elements may be required when extruding THERMOLAST® compounds with high hardness or when coextruding with standard thermoplastics.
Cleaning Recommendation For cleaning and purging of the machine it is appropriate to use polypropylene or polyethylene. Machine must be PVC-free.
The expected shelf life of the TPE granules is a minimum of 24 months from the date of delivery, provided that the storage instructions are followed and the product is kept in the unopened original KRAIBURG TPE packaging.
Dry conditions at room temperature (below 40 °C/ 104 °F), away from heat sources and direct sunlight, must be maintained for proper storage. Contact with nitrogen oxides during storage should be avoided.