TL5NGG-BLCK
THERMOLAST® K
Lightweight applications with adhesion to Polyamides
Processing Method:
Injection Molding
Injection Molding
Color / RAL DESIGN:
black
black
Typical applications
- Function and design elements
- Grip applications
- Bumpers
- Heavy-walled parts
- Seals
Material features
- Low density
- Adhesion to PA6 and PA6.6
- Optimized compression set
- Dry haptics
- Soft, non-sticky haptic
Value | Unit | Standard | |
---|---|---|---|
Hardness | 53 | Shore A | DIN ISO 48-4 |
Density | 0.720 | g/cm3 | DIN EN ISO 1183-1 |
Tensile Strength1 | 2.1 | MPa | DIN 53504/ISO 37 |
Elongation at Break1 | 200 | % | DIN 53504/ISO 37 |
Tear Resistance | 10.0 | N/mm | ISO 34-1 Method B (b) (Graves) |
CS 72 h/23 °C | 10 | % | DIN ISO 815-1 Method A |
CS 24 h/70 °C | 37 | % | DIN ISO 815-1 Method A |
Adhesion to PA 62 | 3.0 (D) | N/mm | VDI 2019 two-component injection molding |
Adhesion to PA 6.62 | 3.0 | N/mm | VDI 2019 two-component injection molding |
1Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min.
2The adhesion quality depends on mold design, product geometry and process parameters.
2The adhesion quality depends on mold design, product geometry and process parameters.
All values published in this data sheet are rounded average values. |
The expected shelf life of the TPE granules is a minimum of 24 months from the date of delivery, provided that the storage instructions are followed and the product is kept in the unopened original KRAIBURG TPE packaging. Dry conditions at room temperature (below 40 °C/ 104 °F), away from heat sources and direct sunlight, must be maintained for proper storage. Contact with nitrogen oxides during storage should be avoided. |
For further information and individual custom solutions please contact our customer service. |
Processing Guideline Injection Molding | |
---|---|
Cylinder Temperature | 180 - 200 - 220 °C, max. 250 °C (360 - 390 - 430 °F, max. 480 °F) |
Hotrunner | Hot runner temperatures: 200 -250 °C (390 - 480 °F). The runner should be empty after a maximum of 2 - 3 shots. |
Injection Pressure | 200 - 1000 bar (2900 - 14504 psi) (depending on the size and weight of the part). |
Injection Rate | In general, the fill time should not be more than 1–2 seconds. |
Hold Pressure | We recommend to derive the optimum hold pressure from determining the solidification point, starting with 40 % - 60 % of the required injection pressure. |
Back Pressure | 20 - 100 bar; if color batches are used, higher back pressure is necessary. |
Screw Retraction | If an open nozzle is used processing with screw retraction is advisable. |
Mold Temperature | The mold temperature depends on the hard component. A temperature exceeding 80 °C (175 °F) should be avoided. The common temperature is 40 - 60 °C (105 - 140° F). |
Predrying | Residual moisture content might lead to processing problems and a reduction in the quality of the finished part. The use of a desiccant dehumidifying dryer is recommended. Drying conditions: 80 °C for 2-4 hrs; maximum dew point of the inlet air: -25 °C. The maximum residual moisture of the material should not exceed 0 ,02%. |
Needle Valve | With materials < 50 Shore A the use of a needle valve is advisable. |
Screw Geometry | Standard 3-zone polyolefine screw. |
Residence Time | The residence time is to be set as short as possible with a maximum of 10 minutes. |
Cleaning Recommendation | For cleaning and purging of the machine it is appropriate to use polypropylene or polyethylene. Machine must be PVC-free. |
Dry conditions at room temperature (below 40 °C/ 104 °F), away from heat sources and direct sunlight, must be maintained for proper storage. Contact with nitrogen oxides during storage should be avoided.