LW/PA Series

THERMOLAST® K

The LW/PA Series is your lightweight material solution for applications with adhesion to PA. The compounds are available in black colors.

Processing Method: Injection Molding
Color / RAL DESIGN: Black

Typical applications

  • Function and design elements
  • Grip applications
  • Bumpers
  • Soft touch
  • Heavy-walled parts

 

Material advantages

  • Low density
  • Adhesion to PA6 and PA12
  • Dry haptics
  • Colorable
  • Soft, non-sticky haptic

 

Please choose language of datasheet
PDF file - 1MBDeutsch
PDF file - 1MBEnglish
PDF file - 1MBEspañol
PDF file - 1MBFrançais
PDF file - 1MBItaliano
PDF file - 1MB日本語
PDF file - 1MB한국어
PDF file - 1MBPolski
PDF file - 1MB中文
X

SHARE FILE

Send
Compound name
Color / RAL DESIGN
Hardness
DIN ISO 48-4
Shore A
Density
DIN EN ISO 1183-1
g/cm3
Tensile Strength 1
DIN 53504/ISO 37
MPa
Elongation at Break 1
DIN 53504/ISO 37
%
Tear Resistance
ISO 34-1 Methode B (b) (Graves)
N/mm
CS 72 h/23 °C
DIN ISO 815-1 Method A
%
CS 24 h/70 °C
DIN ISO 815-1 Method A
%
Adhesion to PA 6 2
VDI 2019 two-component injection molding
N/mm
Adhesion to PA 6.6 2
VDI 2019 two-component injection molding
N/mm
TL5NGG-BLCK Black 53 0.725 2.1 200 10.0 10 37 3.0 (D) 3.0 (D)
TL6NGG-BLCK Black 60 0.725 2.6 250 11.5 15 40 3.4 (D) 3.0 (D)
TL7NGG-BLCK Black 70 0.725 3.3 250 13.0 16 37 3.7 (D) 3.2 (D)
1Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min.
2The adhesion quality depends on mold design, product geometry and process parameters.
All values published in this data sheet are rounded average values.
The product storage life is 12 months after delivery if storage instructions are followed. Store under dry conditions at room temperature (15–30 °C) away from heat sources and direct sunlight! Contact with nitrogen oxides must be avoided during storage!
For further information and individual custom solutions please contact our customer service.