RI6PGM-BLCK
RC/AD1/AP Series | THERMOLAST® R
Hardness-dependent post-industrial recycled content, adhesion to ABS, PC, PC/ABS, for the Asia Pacific market
Processing Method:
Injection Molding
Injection Molding
Color / RAL DESIGN:
black
black
Recycled raw materials content**:
34%
34%
Availability:
Globally
Globally
Manufacturing Site :
Malaysia
Malaysia
Typical applications
- Function and design elements
- Handles and grips for consumer applications
- Handles (tools, toolboxes, ski poles)
- Soft touch surface (thumb wheels, push buttons, switches)
- Games consoles
- Remote controls
- Ear phones
- Household articles
- Wearables
Material advantages
- Optimized mechanical properties
- Non-sticky surface
- Colorable
- Sustainable material
- Recycled raw material content
- Adhesion to PC, ABS, PC/ABS
- Smooth touch
Value | Unit | Standard | |
---|---|---|---|
Hardness | 62 | Shore A | DIN ISO 48-4 |
Density | 1.060 | g/cm3 | DIN EN ISO 1183-1 |
Tensile Strength1 | 6.0 | MPa | DIN 53504/ISO 37 |
Elongation at Break1 | 480 | % | DIN 53504/ISO 37 |
Tear Resistance | 21.0 | N/mm | ISO 34-1 Method B (b) (Graves) |
Adhesion to ABS2 | 2.5 (B) | N/mm | VDI 2019 two-component injection molding |
Adhesion to PC2 | 3.0 (B) | N/mm | VDI 2019 two-component injection molding |
1Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min. Specimens were tempered for 20 hrs at 100°C (212°F).
2The adhesion quality depends on mold design, product geometry and process parameters.
2The adhesion quality depends on mold design, product geometry and process parameters.
**Recycling-specific influences such as slight color deviations, gloss differences, viscosity variations or a higher hardness spreading are possible with TPEs containing a recycled component. |
All values published in this data sheet are rounded average values. |
The shelf life of the TPE granules is 24 months from delivery if storage instructions are observed and the product is stored in the unopened original KRAIBURG TPE packaging. Store in dry conditions at room temperature (below 40 °C) away from heat sources and direct sunlight! Contact with nitrogen oxides must be avoided during storage! |
For further information and individual custom solutions please contact our customer service. |
Processing Guideline Injection Molding | |
---|---|
Cylinder Temperature | 180 - 190 - 200 °C, max. 220 °C (360 - 370 - 390 °F, max. 425 °F) |
Hotrunner | Hot runner temperatures: 180 - 220 °C (356 - 428 °F). The runner should be empty after a maximum of 2 - 3 shots. |
Injection Pressure | 200 - 1000 bar (2900 - 14504 psi) (depending on the size and weight of the part). |
Injection Rate | In general, the fill time should not be more than 1–2 seconds. |
Hold Pressure | We recommend to derive the optimum hold pressure from determining the solidification point, starting with 40 % - 60 % of the required injection pressure. |
Back Pressure | 20 - 100 bar; if color batches are used, higher back pressure is necessary. |
Screw Retraction | If an open nozzle is used processing with screw retraction is advisable. |
Mold Temperature | The mold temperature depends on the hard component. A temperature exceeding 80 °C (175 °F) should be avoided. The common temperature is 40 - 60 °C (105 - 140° F). |
Predrying | The material is hygroscopic, residual moisture content might lead to processing problems and a reduction in the quality of the finished part. The use of a desiccant dehumidifying dryer is recommended. Drying conditions: 80 °C for 4-6 hrs; maximum dew point of the inlet air: -25 °C. The maximum residual moisture of the material should not exceed 0,02 %. |
Needle Valve | The use of a needle valve nozzle is advisable . |
Screw Geometry | Standard 3-zone polyolefine screw. |
Residence Time | The residence time is to be set as short as possible with a maximum of 10 minutes. |
Cleaning Recommendation | For cleaning and purging of the machine it is appropriate to use polypropylene or polyethylene. Machine must be PVC-free. |