AD/PA/CS Series

THERMOLAST® K

The AD/PA/CS series is your material solution for applications with excellent adhesion to PA and sealing function. The compounds are available in black and natural colors. Natural color variants can be colored in many different ways.

Processing Method: Injection Molding, Extrusion
Color / RAL DESIGN: Natural, Black

Typical applications

  • Seals
  • Fastenings
  • Grommets
  • Cable clips
  • Membranes

 

Material features

  • Adhesion to PA6 and PA6.6, up to 50% glass fiber
  • Optimized compression set
  • Optimized flow properties

 

Regulations / Approvals *

  • VW 50123
  • BMW GS 93042
  • Mercedes-Benz DBL 5562
  • Stellantis B62 0300
  • Renault 03-10-104
  • GM GMW15702
  • UL 94 HB

 

Please choose language of datasheet
PDF file - 1MBDeutsch
PDF file - 1MBEnglish
PDF file - 1MBEspañol
PDF file - 1MBFrançais
PDF file - 1MBItaliano
PDF file - 1MB日本語
PDF file - 1MB한국어
PDF file - 1MBPolski
PDF file - 1MB中文
X

SHARE FILE

Send
Compound name
Color / RAL DESIGN
Hardness
DIN ISO 48-4
Shore A
Density
DIN EN ISO 1183-1
g/cm3
Tensile Strength 1
DIN 53504/ISO 37
MPa
Elongation at Break 1
DIN 53504/ISO 37
%
Tear Resistance
ISO 34-1 Method B (b) (Graves)
N/mm
CS 72 h/23 °C
DIN ISO 815-1 Method A
%
CS 24 h/70 °C
DIN ISO 815-1 Method A
%
CS 24 h/100 °C
DIN ISO 815-1 Method A
%
Adhesion to PA 6 2
VDI 2019 two-component injection molding
N/mm
Adhesion to PA 6.6 2
VDI 2019 two-component injection molding
N/mm
Short term temperature stability under stress -40°C up to
KRAIBURG TPE test method
°C
Short term temperature stability without stress -40°C up to
KRAIBURG TPE test method
°C
Long term temperature stability without stress from -40°C up to
KRAIBURG TPE test method
°C
TC4PCN Natural 37 1.100 2.5 300 9.0 20 31 47 3.0 (D) 3.0 (D) 100 150 120
TC4PCZ Black 35 1.100 2.5 350 8.5 20 35 50 3.0 (D) 3.0 (D) 100 150 120
TC5PCN Natural 47 1.100 4.0 350 11.5 20 32 45 4.5 (D) 4.5 (D) 110 150 120
TC5PCZ Black 45 1.100 4.0 400 11.5 22 37 50 4.5 (D) 4.5 (D) 110 150 120
TC6PCN Natural 57 1.100 5.0 350 15.5 21 38 50 4.5 (D) 4.5 (D) 100 150 125
TC6PCZ Black 57 1.100 5.0 400 16.0 25 40 50 5.5 (D) 5.5 (D) 100 150 125
TC7PCN Natural 67 1.100 7.0 400 16.0 25 40 56 6.5 (D) 5.5 (D) 100 150 125
TC7PCZ Black 66 1.100 7.5 400 19.0 25 40 55 5.5 (D) 7.0 (D) 100 150 125
TC8PCN Natural 77 1.100 8.5 400 24.0 25 40 58 8.0 (D) 8.5 (D) - - -
TC8PCZ Black 75 1.100 9.0 450 24.5 29 44 61 7.0 (D) 8.0 (D) - - -
1Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min.
2The adhesion quality depends on mold design, product geometry and process parameters.
All values published in this data sheet are rounded average values.
The expected shelf life of the TPE granules is a minimum of 24 months from the date of delivery, provided that the storage instructions are followed and the product is kept in the unopened original KRAIBURG TPE packaging.
Dry conditions at room temperature (below 40 °C/ 104 °F), away from heat sources and direct sunlight, must be maintained for proper storage. Contact with nitrogen oxides during storage should be avoided.
For further information and individual custom solutions please contact our customer service.
* Regulations a compound complies with and approvals granted are displayed here. Please note: All regulations and approvals for all compounds of a series are collectively shown in the overview of the respective product series, i.e. not all regulations and approvals shown in the overview apply to each individual compound.